| Resistance To Corrosion: | Excellent | Heat Resistance: | High |
|---|---|---|---|
| モース硬度: | 7〜8 | Water Absorption: | ≤20% |
| Heat Capacity: | High | 経験: | 30年 |
| Thermal Expansion: | Low | ポイント: | 高アルミナ質耐火れんが |
| Size: | 230x114x65mm or Customized | Bulk Density: | ≥ 2.6 g/cm3 |
| 折りたたみの強さ: | >20MPa | Cold Crushing Stren: | 45-80 |
| Apparent Porosity: | ≤ 22% | 衝撃耐性: | 高い |
| Ccs Strength: | 45 | ||
| ハイライト: | Wear Resistance Alumina Refractory Brick,Phosphate Bonded Alumina Refractory Brick |
||
Refractory manufacturer supply wear resistance phosphate bonded alumina refractory brick
Phosphate bonded high alumina bricks are made from high alumina bauxite aggregate, selecting phosphoric acid or aluminum phosphate as binder. Finished phosphate bonded high alumina brick must go through 400~600 ℃ heating process and semi-dry compress process. Featured by high wear-resistance, high refractoriness and good thermal shock resistance, phosphate bonded high alumina bricks are widely used in rotary cement kiln transition zone, sintering zone, cooling zone and cooler working layer.
Phosphate Bonded High Alumina Bricks Features:
High mechanical strength
High refractoriness
Good wear resistance
Good spalling resistance
Phosphate Bonded High Alumina Brick Parameters
| Item | Specification | ||
| PA | PW | SP | |
| Al2O3 % | ≥75 | ≥77 | ≥80 |
| Fe2O3 % | ≤2.5 | ≤2.1 | ≤1.8 |
| CCS, MPa | ≥70 | ≥75 | ≥80 |
| Bulk Density, g/cm3 | ≥2.70 | ≥2.65 | ≥2.90 |
| 0.2MPa RUL℃ | ≥1350 | ≥1300 | ≥1520 |
| TSR, Cycle 1100℃ Water | ≥20 | ≥20 | ≥20 |
Phosphate Bonded High Alumina Bricks Application
1.Glass melting furnace, ceramic frit kiln, sodium silicate furnace, soaking furnace, ceramic kiln, etc
2.Coke oven’s coking chamber, combustion chamber walls, steel open-hearth ‘s regenerator and sediment chamber, etc.
3.Load-bearing parts of high temperature hot air furnace and acid open-hearth furnace roof, etc.