| 見かけの多孔性: | 22％以下 | 密度: | 2.2-2.4 g/cm3 |
|---|---|---|---|
| アイテム: | ハイアルミナレンガ | 軟化温度: | ≥1400℃ |
| 耐摩耗性: | 高い | サービス温度: | 高い |
| 耐食性: | 高い | 負荷下の屈折率: | ≥1520℃ |
| 応用: | 高温炉の裏地 | 温度: | 1700-1800℃ |
| 永続的な線形変化: | 低い | アルカリ抵抗: | 高い |
| CCS強度: | 45 | 酸耐性: | 高い |
| 表面: | スムーズ | ||
| ハイライト: | high alumina refractory brick for electric arc furnace,48-90% Al2O3 alumina silica fire brick,230x114x65mm high alumina refractory brick |
||
High Quality 48-90% Al2O3 Alumina Silica Fire Brick 230*114*65mm High Alumina Refractory Bricks for Electric Arc Furnace Roof
High Alumina Refractory Bricks
High alumina bricks refer to aluminosilicate refractory products with aluminum oxide (Al2O3) content higher than 48%. It belongs to neutral refractory material. It is formed by shaping and calcining bauxite or other raw materials with high alumina content. High thermal stability and fire resistance above 1770 ℃. It has good slag resistance and is used for lining steel making electric furnace, glass furnace, cement rotary furnace, etc.
High load soft and low creep high alumina brick is a high-grade refractory material made of special grade bauxite, fused corundum and fused mullite. The product has the advantages of small high-temperature creep, strong corrosion resistance, good thermal shock stability, etc. It is suitable for large and medium-sized hot blast furnaces.
High Alumina Refractory Bricks Advantage
1. High refractoriness;
2. High temperature strength;
3. High thermal stability;
4. Neutral refractory;
5. Good resistance to acid and basic slag corrosion;
6. High refractoriness under load;
7. High temperature creep resistance;
8. Low apparent porosity;
High Alumina Refractory Bricks Application
As a basic material in the field of high-temperature technology, high alumina bricks are widely used in cement, glass building materials, steel smelting, petrochemical and other industries. High temperature industrial furnaces for high alumina bricks include blast furnace, hot blast furnace, electric furnace, blast furnace, reverberatory furnace and rotary kiln lining. In addition, high alumina bricks can also be processed into open hearth regenerative grid bricks, socket bricks for pouring system, nozzle bricks, etc. according to the requirements of industrial furnaces.
High Alumina Refractory Brick Physical and Chemical Index:
| Item/Grade | Fire Clay Brick | High Alumina Brick | ||||||
| SK-30 | SK-32 | SK-34 | SK-35 | SK-36 | SK-37 | SK-38 | SK-40 | |
| AL2O3% (≥) | 30 | 35 | 38 | 45 | 55 | 65 | 70 | 82 |
| Fe2O3% (≤) | 2.5 | 2.5 | 2 | 2 | 2 | 2 | 2 | 2 |
| Refractoriness(SK) | 30 | 32 | 34 | 35 | 36 | 37 | 38 | 40 |
| Refractoriness Under Load, 0.2MPa, °C (≥) | 1250 | 1300 | 1360 | 1420 | 1450 | 1480 | 1530 | 1600 |
| Apparent Porosity (%) | 22-26 | 20-24 | 20-22 | 18-20 | 20-23 | 20-23 | 20-22 | 18-20 |
| Bulk Density (g/cm³) | 1.9-2.0 | 1.95-2.1 | 2.1-2.2 | 2.15-2.22 | 2.25-2.4 | 2.3-2.5 | 2.4-2.6 | 2.5-2.7 |
| Cold Crushing Strength ,MPa (≥) | 20 | 25 | 30 | 40 | 45 | 50 | 60 | 70 |
| Brick Standard Sizes | |||||
| SPLITSTRAIGHT L×W×H(mm) |
SPLIT L×W×H(mm) |
ARCH L×W×H(mm) |
WEDGE L×W×H(mm) |
TILE L×W×H(mm) |
OTHER SHAPE |
| 230×114×65 | 230×114×25 | 230×114×65/45 | 230×114×65/45 | 230×230×38 | Key brick |
| 230×114×75 | 230×114×32 | 230×114×65/55 | 230×114×65/55 | 230×230×50 | Skew brick |
| 230×114×37 | 230×114×75/45 | 220×114×75/45 | 230×230×65 | Soap | |
| 230×114×50 | 230×114×75/55 | 220×114×75/55 | 230×230×75 | Checker | |
| ≤10 | 230×114×75/65 | 220×114×75/65 | Neck | ||
| Taper | |||||
| Application | Steel furnace, glass furnace, sodium silicate furnace, ceramic shuttle kiln, cement rotary kiln, blast furnace, electric furnace,blast furnace and reverberatory furnace. | ||||
| We also can make brick according to customers’ drawing and requirements. | |||||