| 原材料: | 鋼玉石およびムライト | カスタマイズされた: | はい |
|---|---|---|---|
| 設置方法: | 振動鋳造 | 破裂の強さ: | ≥6Mpa 1100°C×3h で |
| 使用法: | 炉ライナー、作業ライニング鋳造 | 曲げ強度: | 1d ≥6.0MPa |
| 耐久性: | 1700℃以上 | 製品: | 酸耐性キャスト可能 |
| 使用温度: | 1800℃ | 圧縮強度: | ≧50MPa（3日間硬化後） |
| アプリケーション: | コックスオーブン | アプリケーション 温度: | 最大1800°C |
| タイプ: | 製造 | 製造された: | エナン |
| アルミナコンテンツ: | 50％ | ||
| ハイライト: | high temperature refractory gunning mix,alumina silicate spray coatings,induction furnace refractory castable |
||
Rongsheng Refractory Gunning Materials High Refractoriness Alumina Silicate Spray Coatings Induction Furnace Refractory Gunning Mix
Refractory Gunning Mix:
Gunning mix is composed of refractory aggregate, refractory powder, water, binder, mineralizer, plasticizer, and firing aid. It is a fire-resistant mixture constructed by spraying method.The materials of gunning mix include silicon aluminum, magnesium, corundum, and phosphate. It is also divided into lightweight,medium heavy weight and heavy weight gunning mix.
Light weight gunning mix is used for thermal insulation and insulation lining, medium heavy weight can be used as both thermal insulation and working lining for mediuContact Usm and low temperature furnaces, heavy weight gunning mix is mainly used as working lining.
Features and Advantages of Refractory Gunning Mix
refractory gunning mix has the characteristics of high adhesive rate,less resilience,high strength and easy gunning etc.scour resistance,impact resistance,erosion resistance.anti-scouring, wear resistance and excellent performances.
Application of Refractory Gunning Mix
Steel Industry,Energy Industry,Building Materials.It serves as a protective layer on the inner surface of blast furnace and hot blast furnace shells, as well as a working lining for blast furnace heads, coal gas outlet pipe, and dust collectors.
Refractory Material Gunning Mix Technique Data
| Item | Specification | |||
| LGP0.8 | LGP1.0 | LGP1.3 | ||
| Al2O3 % | ≥30 | ≥35 | ≥40 | |
| Bulk Density,g/cm3 110℃×24h | ≤0.8 | ≤1.0 | ≤1.3 | |
| CCS, MPa | 110℃×24h | ≥4 | ≥5 | ≥7 |
| Test Temperature, ×3h | ≥3 800℃ | ≥4 1000℃ | ≥5 1200℃ | |
| PLC, % Test Temperature, ×3h |
±0.8 800℃ |
±0.8 1000℃ |
±0.8 1200℃ |
|
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.21 | ≤0.25 | ≤0.35 | |
| Test Temperature, ℃ | 800 | 1000 | 1200 | |
| Item | Specification | |||
| LGP1.5 | LGP1.8 | LGP1.8T | ||
| Al2O3 % | ≥42 | ≥45 | ≥55 | |
| Bulk Density,g/cm3 110℃×24h | ≤1.5 | ≤1.8 | ≤1.8 | |
| CCS, MPa | 100℃×24h | ≥12 | ≥15 | ≥12 |
| Test Temperature, ×3h | ≥10 1300℃ | ≥13 1300℃ | ≥10 1400℃ | |
| PLC, % Test Temperature×3h |
±0.8 1300℃ |
±0.8 1300℃ |
±1.0 1400℃ |
|
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.4 | ≤0.7 | ≤0.75 | |
| Max Working Temperature, ℃ | 1300 | 1300 | 1500 |
|